JUSHI 440 Assembled Roving for SMC

440 is a general purpose SMC roving coated with a silane-based sizing compatible with unsaturated polyester and vinyl ester resins.

440 is suitable for use in producing low and ultra-low shrinkage sheets to be incorporated typically in automotive parts, door skins, water tanks and electrical components.

Product Features

• Good anti-static property
• Excellent choppability and wet-out
• Excellent strength of parts

Specification

Glasstype	E
Sizingtype	Silane
Typicalfilamentdiameter(μm)	14 / 15 / 16
Typicallineardensity(tex)	2400 / 4400 / 4800
Example	ER14-2400-440

Technical Parameters

Item	Linear density variation	Moisture content	Sizing content	Stiffness
Unit	%	%	%	mm
Test menthod	ISO1889	ISO3344	ISO1887	ISO 3375
Standard range	±4	≤0.07	1.25±0.15	160±20（14μm~15μm） 170±20(16um;440(80))

Instructions

• The product is best used within 12 months after production, and should be kept in the original package before use.
• Care should be taken when using the product to prevent it from being scratched or damaged.
• The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
• When using the product, please control the tension properly and ensure the tension uniformity.

Packaging

For detailed package size information, please download the product manual to view!

Storage

Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10℃~35℃ and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.