310H Direct Roving or Assembled Roving is produced by using E6 glass formulation and coated with a silane-based sizing. It is specially designed for the reinforcement of epoxy resin.It is designed for filament winding and pultrusion applications and suitable for use in insulation rods and insulating pipe.
310H offers a fast and complete wet-out of resin. The composites it reinforces have excellent mechanical,electrical insulation and acid corrosion resistance properties.It is suitable for use in UHV and EHV power transmission,transformation and other fields.
Product Features
- Excellent process performance and low fuzz
- Multi-resin compatibility
- Excellent mechanical properties of parts, good resistance to heat bending
- Excellent chemical corrosion resistance
Specification
| Glasstype | E6 | ||
| Sizingtype | Silane | ||
| Typicalfilamentdiameter(μm) | 17 | 24 | |
| Typicallineardensity(tex) | 1200 2400 9600 19200 | ||
| Example (Direct Roving) | E6DR24-2400-310H | ||
| Example (Assembled Roving) | E6R-19200-310H | ||
Technical Parameters
| Item | Linear density variation | Moisture content | Sizing content | Breakage strength |
| Unit | % | % | % | N/tex |
| Test menthod | ISO1889 | ISO3344 | ISO1887 | ISO 3341 |
| Standard range | ±5(Direct Roving<600 tex)±4(Direct Roving≥600 tex )±4(Assembled Roving) | ≤0.07 | 0.55±0.10 | ≥0.40(<4800 tex) ≥0.30(≥4800 tex) |
Mechanical Properties
| Mechanical properties | Unit | Value | Resir | Test menthod |
| Tensile strengtt | MPa (Ksi) | 2316 | EP | ASTM D2343 |
| Tensile modulus | GPa (Msi) | 82.2 (11.9) | EP | ASTM D2343 |
Instructions
- The product is best used within 12 months after production, and should be kept in the original package before use.
- Care should be taken when using the product to prevent it from being scratched or damaged.
- The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
- When using the product, please control the tension properly and ensure the tension uniformity.
Packaging
For detailed package size information, please download the product manual to view!
Storage
Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10℃~35℃ and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.