JUSHI 362H Direct Roving for LFT

Ready to experience high-quality products at a price that works for you? Contact us for a quote today!

362H direct roving is specially designed forlong fiberglass thermoplastics(LFT) and compatiblewith modified PP resin.

362H is suitable forboth LFT-D(long fiberglass reinforced thermoplastics direct/in-linecompounding)andLFT-G(granulate)andfindswideusagein

automotive,electricalandelectronics,communications,andsportsandmedical devices.

Product Features

  • Lowfuzz
  • Excellent compatibility with multiple thermoplastic resins
  • Goodprocess performance
  • Excellent mechanicalproperties

Specification

GlasstypeE
SizingtypeSilane
Typicalfilamentdiameter(μm)17
Typicallineardensity(tex)2400
Example EDR17-2400-362H

Technical Parameters

ItemLinear density variationMoisture contentSizing contentBreakage strength
Unit%%%N/tex
Test menthodISO1889ISO3344ISO1887ISO 3341
Standard range±5(<600 tex) ±4(≥600 tex)0.070.35±0.10≥0.35

Instructions

  • The product is best used within 12 months after production, and should be kept in the original package before use.
  • Care should be taken when using the product to prevent it from being scratched or damaged.
  • The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
  • When using the product, please control the tension properly and ensure the tension uniformity.

Packaging

For detailed package size information, please download the product manual to view!

Storage

Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10~35and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.