JUSHI 396 Direct Roving for Filament Winding&Weaving

Ready to experience high-quality products at a price that works for you? Contact us for a quote today!

396 Direct Roving is based on E-glass formulation and coated with a silane-based sizing.It is compatible with polyester,vinyl ester,epoxy,and polyurethane resin systems.It ismainly designed for weaving and stitching,as well as for filament winding and pultrusionprocesses.

396 has excellent resin compatibility.It is suitable for prepreg and vacuum-assisted resin infusion processes to manufacturelarge wind blades,and also for winding and pultrusion processes to make utility poles,container doors and panels,etc.

Product Features

  • High process flexibility
  • Multi-resin compatibility
  • Fast and complete wet-out
  • Excellent acid corrosion resistance

Specification

Glass typeE6
Sizing typeSilane
Typical filament diameter (μm)131721
Typical linear density (tex)300600
1200
2400

2000
ExampleEDR17-2400-396

Technical Parameters

ltemLinear density variation (%)Moisture content (%)Sizing content (%)Breakage strength (N/tex)
Test methodISO 1889ISO 3344/SO 1887ISO 3341

Standard range
±4≤0.070.48~0.10≥0.40

Mechanical  properties

Mechanical  propertiesUnitValueResinTest menthod

Tensile  strength
MPa2471UP/EPASTM D2343
Tensile  modulusGPa81.3UP/EPASTM D2343
Shear strengthMPa67EPASTM D2344
Strength retention(72 hr boiling)%>96EP/

Instructions

  • The product is best used within 12 months after production, and should be kept in the original package before use.
  • Care should be taken when using the product to prevent it from being scratched or damaged.
  • The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
  • When using the product,please control the tension properly and ensure the tension uniformity.

Packaging

For detailed package size information, please download the product manual to view!

Storage

Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10~35and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.