JUSHI 352B Direct Roving for LFT

352B Direct Roving for LFTis coated with a silane-based sizingcompatiblewith such resins asPAandTPU.

352B is designed for LFT-G and LFT-D processes.Its superior compatibility with matrix

resinmakesitfavoredinautomotive,electrical&electronic,telecommunications,construction,andsportsindustries.

Product Features

• Lowfuzz
• Excellent compatibility with multiple thermoplastic resins
• Goodprocess performance
• Excellent mechanicalproperties
  

Specification

Glasstype	E
Sizingtype	Silane
Typicalfilamentdiameter(μm)	16	17
Typicallineardensity(tex)	600 2200	2400
Example	EDR17-2400-352B

Technical Parameters

Item	Linear density variation	Moisture content	Sizing content	Breakage strength
Unit	%	%	%	N/tex
Test menthod	ISO1889	ISO3344	ISO1887	ISO 3341
Standard range	±5(<600 tex) ±4(≥600 tex)	≤0.07	0.35±0.10	≥0.35

Instructions

• The product is best used within 12 months after production, and should be kept in the original package before use.
• Care should be taken when using the product to prevent it from being scratched or damaged.
• The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
• When using the product, please control the tension properly and ensure the tension uniformity.

Packaging

For detailed package size information, please download the product manual to view!

Storage

Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10℃~35℃ and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.