362J direct roving is specially designed to reinforce modified PP resin in the LFT (long fiber thermoplastics) process.
362J is suitable for both LFT-D (direct in-line compounding) and LFT-G (granulate) processes, and widely used in automotive, electrical and electronic,
communication, sports, and medical equipment.
Product Features
- Lowfuzz
- Excellent compatibility with multiple thermoplastic resins
- Goodprocess performance
- Excellent mechanicalproperties
Specification
| Glasstype | E | |||
| Sizingtype | Silane | |||
| Typicalfilamentdiameter(μm) | 17 | |||
| Typicallineardensity(tex) | 2400 | |||
| Example | EDR17-2400-362J | |||
Technical Parameters
| Item | Linear density variation | Moisture content | Sizing content |
| Unit | % | % | % |
| Test menthod | ISO1889 | ISO3344 | ISO1887 |
| Standard range | ±5(<600 tex) ±4(≥600 tex) | ≤0.07 | 0.40±0.10 |
Instructions
- The product is best used within 12 months after production, and should be kept in the original package before use.
- Care should be taken when using the product to prevent it from being scratched or damaged.
- The temperature and humidity of the product should be balanced with the ambient temperature and humidity before use, and theambient temperature and humidity should be properly controlled during the use.
- When using the product, please control the tension properly and ensure the tension uniformity.
Packaging
For detailed package size information, please download the product manual to view!
Storage
Unless otherwise specified, the fiberglass products should be stored in a dry,cool and moisture-proof area.The best temperature and humidity should be maintained at -10℃~35℃ and ≤80% respectively. To ensure safety and avoid damage to the product, the pallets should be stacked not more than three layers high. When the pallets are stacked in two or three layers, special care should be taken to correctly and smoothly move the upper pallet.